| Material Item | Aluminum oxide | ZTA | Zirconia |
|---|---|---|---|
| Volume density (g/cm³) | 3.9 | 4.17 | 6.0 |
| Vickers hardness (GPa) | 13 | 12 | 11 |
| Bending strength (MPa) | 350 | 480 | 800 |
| Fracture tenacity (MPa.m1/2) | 4 | 5 | 9 |
| Abrasion resistance (min/cm³) | 15 | 35 | 40 |
Specializing in the research and development, design, manufacturing, and sales of alumina special ceramics. The facility features specialized production lines for alumina ceramic grinding media including alumina balls, lining bricks, and high-purity inert filler balls (92%, 95%, 99%).
Compared with metal grinding bodies, our ceramic products feature high temperature resistance, high hardness, high strength, low wear, and corrosion resistance. They are designed to solve problems associated with non-metallic grinding bodies such as high wear and breakage, effectively reducing maintenance costs and achieving energy conservation goals.